| PRODUCT DATA of 18 Ni Maraging steel, 300 grade |
| Material | 18 Ni Maraging steel, 300 grade |
| General Information | Annealed for one hour at 1500° F, air cooled and aged at 900° F for three hours Manufacturer datasheet |
| Processing and Assembly | In the solution annealed condition (as supplied to the customer), they are very tough, relatively soft (30/35 R c ), and therefore, readily machined and formed. After machining or forming, a precipitation hardening (aging) process, which requires no protective atmosphere and relatively low furnace temperatures, raises the hardness to a level sufficient for many tooling applications. |
| Chemical Composition | Fe-18.5Ni-9Co-4.8Mo-0.6Ti |
| EXPERIENCE IN PRACTICE |
|---|
| Equivalent Designations | Maraging 300; Maraging C300; Vascomax C300 |
| PHYSICAL PROPERTIES |
|---|
| Specific Gravity | 8 |
| ELASTIC PROPERTIES |
|---|
| Tensile Modulus | 190 GPa |
| THERMAL PROPERTIES |
|---|
| Thermal Conductivity | 25.3 W/m.K |
| Thermal Expansion Coefficient | 10.1 μstrain/°C |
| RELEVANT PROPERTIES FOR USE IN SPACE COMMUNITY |
|---|
| Stress Corrosion Status | Low Resistance to SCC: Table 3
Remark: Not for primary structural items Remark: Requires Stress corrosion evaluation form Remark: acc. to ECSS-Q-ST-70-36C Data Quality: Design Data |