| All data is for information only------(<---links) | |
|---|---|
| PRODUCT DATA of 15-5PH H900 |
| Material | 15-5PH H900 |
| Product Datasheet | AMI SMC AK Steel Bohler |
| General Information | 15-5PH is a precipitation-hardening, martensitic stainless steel used for parts requiring corrosion resistance and high strength at temperatures up to 315C. Alloy 15-5PH has good transverse ductility and strength in large section sizes. This material is supplied in either the annealed or overaged condition and is heat treated after fabrication |
| Processing and Assembly | cold worked and aged at 480C |
| Precautions | Parts should never be used in annealed condition. |
| Name of Manufacturer | Boehler Edelstahl GMBH & Co KG
Mariazeller Straße 25, A-8605 Kapfenberg, Austria +43-3862/20-7181 +43 3862/20-7576 info@bohler-edelstahl.com www.bohler-edelstahl.com Aubert and Duval 22, rue Henri-Vuillemin • 92230 Gennevilliers - France 33 (0)1 55 02 58 00 33 (0)1 55 03 58 01 dircom@aubertduval.com www.aubertduval.com |
| EXPERIENCE IN PRACTICE |
|---|
| Development Status | Commercial Product |
| Equivalent Designations | S15500, 1.4545, Z7CNU15.05, N701, X15U5W |
| Space Experience | Good |
| PHYSICAL PROPERTIES |
|---|
| Specific Gravity | 7.81 |
| Magnetic Properties | Ferromagnetic |
| ELASTIC PROPERTIES |
|---|
| Tensile Modulus | 196 GPa |
| THERMAL PROPERTIES |
|---|
| Thermal Expansion Coefficient | 10.8 μstrain/°C |
| Melting Range | 1410 to 1440 °C |
| Specific Heat | 0.46 J/g.K |
| RELEVANT PROPERTIES FOR USE IN SPACE COMMUNITY |
|---|
| General Corrosion Status | No specific corrosion protection required |
| Atmospheric Corrosion | The general level of corrosion resistance exceeds that of Types 410 and 431, and is approximately equal to that of 17-4 PH Stainless Steel The general level of corrosion resistance is best in the fully hardened condition, and decreases slightly as the aging temperature is increased. |
| Stress Corrosion Status | Moderate Resistance to SCC: Table 2 Remark: Requires Stress corrosion evaluation form Data Quality: Design Data |
| Machinability | The forming characteristics are good |
| Welding | Can be welded using TIG or eletric arc welding process, but should be performed in annealed condition |