	PRODUCT DATA of AA3004-H32

Material	AA3004-H32
Processing and Assembly	Strain-hardened and stabilized. Applies to products in the magnesium-aluminum class which will age-soften at room temperature after strain-hardening. These products are strainhardened to the desired amount and then subjected to a low temperature thermal operation which results in a improved ductility. The number following this designation indicates the degree of strain-hardening remaining after the stabilization treatment.
Chemical Composition	0.8-1.3Mg, 1-1.5Mn, rem Al

	EXPERIENCE IN PRACTICE

Development Status	Commercial Product
Cost Range	Low
Lot Reproducibility	Good
Equivalent Designations	A-M1G, AA 3004
Space Experience	Good

	PHYSICAL PROPERTIES

Crystal Structure	Face centered cubic (fcc)
Specific Gravity	2.72
Magnetic Properties	Nonmagnetic

	ELASTIC PROPERTIES

Tensile Modulus	69 GPa
Shear Modulus	25 GPa
Poisson Ratio	0.35

	ELECTRICAL PROPERTIES

Electrical Volume Resistivity	4.1e-8 ohm.m
Electrical Conductivity	42 %IACS

	THERMAL PROPERTIES

Thermal Conductivity	163 W/m.K
Melting Range	629 to 654 °C
Specific Heat	0.893 J/g.K

	RELEVANT PROPERTIES FOR USE IN SPACE COMMUNITY

General Corrosion Status	No specific corrosion protection required
Stress Corrosion Status	High Resistance to SCC: Table 1 Data Quality: Design Data
EMF vs SCE	-0.76 V
Bimetallic Corrosion	Can be used in a non-controlled environment: Al alloys, Cd Can be used in a clean room environment: Mg, Sn-Pb alloys (all), Sn, Pb, Zn, Be Needs specific measures: All others Data Quality: Design Data